Beilstein J. Nanotechnol. 2014, 5, 1073–1081, doi:10.3762/bjnano.5.120
Figure 1: (a) Low magnification and (b) high magnification SEM images of graphite oxide flakes.
Figure 2: AFM and KPFM images of (a) and (b) a GO flake (2 × 2 μm); (c) and (d) a GO-Cs flake (1.4 × 1.4 μm).
Figure 3: (a) XPS survey spectrum of GO (blue line) and GO-Cs (red line); High resolution XPS C1s spectra of ...
Figure 4: Raman spectra of GO-Cs and GO, displaying intense D and G peaks at ≈1380 and ≈1600 cm−1, respective...
Figure 5: Response of the GO and GO-Cs based sensors as a function of NO2 concentration. The inset shows the ...
Figure 6: Response of (a) GO-Cs and GO based sensors towards NO2 with concentrations higher than 1 ppm; (b) G...
Beilstein J. Nanotechnol. 2012, 3, 378–387, doi:10.3762/bjnano.3.44
Figure 1: Images of TiO2 particles by SEM (a) and by TEM (b, c) as well as XRD pattern of the TiO2 particles ...
Figure 2: J–V characteristics of the dye-sensitized solar cells made from paste A containing 13 wt % TiO2 sph...
Figure 3: Equivalent circuit (a) and the Nyquist plot (b) and Bode plot (c) of the impedance spectrum of a dy...
Figure 4: Comparison of the effective electron lifetime, τn, (a) and effective electron diffusion coefficient...
Figure 5: Comparison of dye-sensitized solar cells based on hierarchically structured TiO2 spheres with and w...